EN X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400

Grades | Stainless Steels | X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400

EN X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400 ( Precipitation-Hardening )

PDF | Word | Print

X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400 Application:Steel, Corrosion-Resistant, Investment Castings 16Cr - 4.1Ni - 0.28Cb (Nb) - 3.2Cu Homogenization, Solution, and Precipitation Heat Treated (H1100) 130 ksi (896 MPa) Tensile Strength (17-4)

Chemical composition(mass fraction)(wt.%) of the X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400
Elements Min.（≥） Max.（≤） Similar Remarks
C - 0.07
Si - 1.00
Mn - 1.00
Cr 15.00 17.50
Ni 3.00 5.00
Cu 3.00 5.00
Nb 0.15 1.45

Mechanical properties of grade X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400

Yield
Rp0.2 (MPa)		 Tensile
Rm (MPa)		 Impact
KV (J)		 Elongation
A (%)		 Reduction in cross section on fracture
Z (%)		 As-Heat-Treated Condition HBW
579 (≥) 149 (≥) 24 24 23 Solution and Aging, Annealing, Ausaging, Q+T,etc 222

Physical properties of grade X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400

Property Density
kg/dm3		 Temperature T
°C/F		 Specific heat
J / kgK		 Thermal conductivity
W/mK		 Electric resistance
µΩ·cm
152 (≥) 445 (≥) 34 23 44 Solution and Aging, Annealing, Ausaging, Q+T,etc
Temp.
°C/°F		 Creep strain limit
(10000h)
(Rp1,0) N/mm2		 Creep rupture strength
(10000h)
(Rp1,0) N/mm2		 - - -
196 914 984 - - -

X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400 Range of products
Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED