GOST 38H2N2MA

Grades | Stainless Steels | 38H2N2MA

GOST 38H2N2MA

PDF | Word | Print

38H2N2MA Application:Structural alloy steel bars. Specifications

Chemical composition(mass fraction)(wt.%) of the 38H2N2MA
Elements Min.（≥） Max.（≤） Similar Remarks
C 0.33 0.40
Si 0.17 0.37
Mn 0.25 0.50
Ni 1.30 1.70
S - 0.025
P - 0.025
Cr 1.3 1.7
Mo 0.20 0.30
Cu - 0.30

Mechanical properties of grade 38H2N2MA

Yield
Rp0.2 (MPa)		 Tensile
Rm (MPa)		 Impact
KV (J)		 Elongation
A (%)		 Reduction in cross section on fracture
Z (%)		 As-Heat-Treated Condition HBW
964 (≥) 725 (≥) 12 14 12 Solution and Aging, Annealing, Ausaging, Q+T,etc 121

Physical properties of grade 38H2N2MA

Property Density
kg/dm3		 Temperature T
°C/F		 Specific heat
J / kgK		 Thermal conductivity
W/mK		 Electric resistance
µΩ·cm
788 (≥) 728 (≥) 42 23 11 Solution and Aging, Annealing, Ausaging, Q+T,etc
Temp.
°C/°F		 Creep strain limit
(10000h)
(Rp1,0) N/mm2		 Creep rupture strength
(10000h)
(Rp1,0) N/mm2		 - - -
893 145 542 - - -

38H2N2MA Range of products
Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED