Grades | Stainless Steels | ЖC6K
GOST ЖC6K
PDF | Word | Print
ЖC6K Application:Russia TY standard grades and chemical compositions of the high temperature alloy castings
Elements | Min.(≥) | Max.(≤) | Similar | Remarks |
---|---|---|---|---|
C | 0.13 | 0.20 | ||
Cr | 9.50 | 12.00 | ||
Al | 5.00 | 6.00 | ||
Mo | 3.50 | 4.80 | ||
Ti | 2.50 | 3.20 | ||
Co | 4.00 | 5.00 | ||
W | 4.50 | 5.50 | ||
Ni | - | remaining | ||
Nb | - | - | ||
Fe | - | 2.00 | ||
B | - | 0.02 | ||
Ce | - | 0.015 | ||
V | - | - | ||
Zr | - | - | ||
Mn | - | 0.40 | ||
Si | - | 0.40 | ||
S | - | 0.015 | ||
P | - | 0.015 | ||
Pb | - | 0.001 | ||
Bi | - | 0.0005 |
Yield Rp0.2 (MPa) |
Tensile Rm (MPa) |
Impact KV (J) |
Elongation A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | HBW |
---|---|---|---|---|---|---|
885 (≥) | 368 (≥) | 33 | 44 | 12 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 231 |
Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
---|---|---|---|---|---|
693 (≥) | 521 (≥) | 44 | 24 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc |
Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
- | - | - |
426 | 553 | 791 | - | - | - |
Product type | Products | Dimension | Processes | Deliver Status |
---|---|---|---|---|
Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |