Grades | Stainless Steels | S.161
B.S. S.161
PDF | Word | Print
S.161 Application:Specification for chromium-nickel-molybdenum corrosion-resisting steel. Bright bars and parts (540 MPa, limiting ruling section 160 mm) (Cr 17.5, Ni 12.5, Mo 2.25, controlled nitrogen content)
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.03 | ||
| Si | - | 1.00 | ||
| Mn | - | 2.00 | ||
| P | - | 0.040 | ||
| S | - | 0.030 | ||
| Cr | 16.50 | 18.50 | ||
| Ni | 11.00 | 14.00 | ||
| Mo | 2.00 | 3.00 | ||
| Nb/Ti | - | - | ||
| N | - | 0.10 |
| Yield Rp0.2 (MPa) |
Tensile Rm (MPa) |
Impact KV (J) |
Elongation A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | HBW |
|---|---|---|---|---|---|---|
| 998 (≥) | 284 (≥) | 43 | 12 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 124 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
|---|---|---|---|---|---|
| 729 (≥) | 387 (≥) | 24 | 22 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
- | - | - |
| 847 | 654 | 623 | - | - | - |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |