Grades | Stainless Steels | PH 14-8 Mo
ASTM PH 14-8 Mo ( Precipitation-Hardening )
PDF | Word | Print
PH 14-8 Mo Application:Sheet and Strip 15Cr - 8,4Ni - 2,2Mo - 1,1Al, vac. Induct. Melted, Solution Heat Treated
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.05 | ||
| Si | - | - | ||
| Mn | - | - | ||
| Cr | 13.50 | 15.50 | ||
| Ni | 7.50 | 9.50 | ||
| Mo | 2.00 | 3.00 | ||
| Co | - | - | ||
| W | - | - | ||
| Al | 0.75 | 1.50 | ||
| Cu | - | - | ||
| Ti | - | - | ||
| Fe | - | - |
| Yield Rp0.2 (MPa) |
Tensile Rm (MPa) |
Impact KV (J) |
Elongation A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | HBW |
|---|---|---|---|---|---|---|
| 864 (≥) | 134 (≥) | 24 | 33 | 34 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 441 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
|---|---|---|---|---|---|
| 564 (≥) | 245 (≥) | 42 | 11 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
- | - | - |
| 993 | 127 | 194 | - | - | - |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |