Grades | Stainless Steels | G10214
AISI G10214 ( Precipitation-Hardening )
PDF | Word | Print
G10214 Application:Free cutting steel
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.05 | ||
| Si | - | 0.20 | ||
| Mn | - | 0.50 | ||
| P | - | - | ||
| S | - | - | ||
| Ni | - | remaining | ||
| Cr | 15.00 | 17.00 | ||
| Al | 4.00 | 5.00 | ||
| Cu | - | - | ||
| Ti | - | 0.50 | ||
| Fe | 2.00 | 4.00 | ||
| N | - | - | ||
| Mo | - | 0.50 | ||
| B | - | 0.006 | ||
| Zr | - | 0.05 |
| Yield Rp0.2 (MPa) |
Tensile Rm (MPa) |
Impact KV (J) |
Elongation A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | HBW |
|---|---|---|---|---|---|---|
| 689 (≥) | 764 (≥) | 24 | 44 | 41 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 224 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
|---|---|---|---|---|---|
| 914 (≥) | 733 (≥) | 33 | 41 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
- | - | - |
| 752 | 838 | 576 | - | - | - |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |