Grades | Stainless Steels | A 29 41L40
SAE A 29 41L40 ( Precipitation-Hardening )
PDF | Word | Print
A 29 41L40 Application:Steel Bars, Carbon and Alloy, Hot-Wrought, General Requirements for
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.01 | ||
| Si | - | 0.20 | ||
| Mn | - | 0.30 | ||
| P | - | - | ||
| S | - | - | ||
| Ni | - | 0.15 | ||
| Cr | 28.00 | 30.00 | ||
| Al | - | - | ||
| Cu | - | 0.15 | ||
| Ti | - | - | ||
| Fe | - | - | ||
| N | - | 0.02 | ||
| Mo | 3.50 | 4.20 |
| Yield Rp0.2 (MPa) |
Tensile Rm (MPa) |
Impact KV (J) |
Elongation A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | HBW |
|---|---|---|---|---|---|---|
| 665 (≥) | 813 (≥) | 23 | 23 | 12 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 422 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
|---|---|---|---|---|---|
| 628 (≥) | 976 (≥) | 33 | 11 | 24 | Solution and Aging, Annealing, Ausaging, Q+T,etc |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
- | - | - |
| 266 | 829 | 875 | - | - | - |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |