Grades | Stainless Steels | 1Cr18Mn10Ni5Mo3N
GB 1Cr18Mn10Ni5Mo3N ( Austenite )
PDF | Word | Print
1Cr18Mn10Ni5Mo3N Application:Of urea with good corrosion resistance, can produce urea corrosion of the equipment.
Chemical composition(mass fraction)(wt.%) of the 1Cr18Mn10Ni5Mo3N
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.10 | ||
| Si | - | 1.00 | ||
| Mn | 8.50 | 12.00 | ||
| P | - | 0.060 | ||
| S | - | 0.030 | ||
| Ni | 4.00 | 6.00 | ||
| Cr | 17.00 | 19.00 | ||
| Mo | 2.8 | 3.5 | ||
| N | 0.20 | 0.30 |
Mechanical properties of grade 1Cr18Mn10Ni5Mo3N
| Yield Rp0.2 (MPa) |
Tensile Rm (MPa) |
Impact KV (J) |
Elongation A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | HBW |
|---|---|---|---|---|---|---|
| 417 (≥) | 263 (≥) | 31 | 42 | 24 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 243 |
Physical properties of grade 1Cr18Mn10Ni5Mo3N
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
|---|---|---|---|---|---|
| 654 (≥) | 285 (≥) | 22 | 42 | 33 | Solution and Aging, Annealing, Ausaging, Q+T,etc |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
- | - | - |
| 783 | 954 | 132 | - | - | - |
1Cr18Mn10Ni5Mo3N Range of products
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |