SAE A 705 S17700

Grades | Stainless Steels | A 705 S17700

SAE A 705 S17700 ( Precipitation-Hardening )

PDF | Word | Print

A 705 S17700 Application:Age-Hardening Stainless Steel Forgings

Chemical composition(mass fraction)(wt.%) of the A 705 S17700
Elements Min.（≥） Max.（≤） Similar Remarks
C - 0.09
Mn - 1.00
Si - 1.00
P - 0.04
S - 0.04
Cr 16.00 18.00
Ni 6.50 7.75
Mo - -
Al 0.75 1.50

Mechanical properties of grade A 705 S17700

Yield
Rp0.2 (MPa)		 Tensile
Rm (MPa)		 Impact
KV (J)		 Elongation
A (%)		 Reduction in cross section on fracture
Z (%)		 As-Heat-Treated Condition HBW
637 (≥) 147 (≥) 43 32 41 Solution and Aging, Annealing, Ausaging, Q+T,etc 443

Physical properties of grade A 705 S17700

Property Density
kg/dm3		 Temperature T
°C/F		 Specific heat
J / kgK		 Thermal conductivity
W/mK		 Electric resistance
µΩ·cm
264 (≥) 678 (≥) 21 33 33 Solution and Aging, Annealing, Ausaging, Q+T,etc
Temp.
°C/°F		 Creep strain limit
(10000h)
(Rp1,0) N/mm2		 Creep rupture strength
(10000h)
(Rp1,0) N/mm2		 - - -
822 288 371 - - -

A 705 S17700 Range of products
Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED