AMS Alloy L605

Grades | Superalloys | Alloy L605

AMS Alloy L605

PDF | Word | Print

Alloy L605 Application:Cobalt Alloy, Corrosion and Heat-Resistant, Welding Wire, 52Co - 20Cr - 10Ni - 15W

Chemical composition(mass fraction)(wt.%) of the Alloy L605
Elements Min.（≥） Max.（≤） Similar Remarks
C 0.05 0.15
Mn 1.00 2.00
P - 0.40
S - 0.03
Si - 0.40
Cr 19.00 21.00
Ni 9.00 11.00
Co - Bal
Fe - 3.0
W 14.00 16.00

Mechanical properties of grade Alloy L605

Yield
Rp0.2 (MPa)		 Tensile
Rm (MPa)		 Impact
KV (J)		 Elongation
A (%)		 Reduction in cross section on fracture
Z (%)		 As-Heat-Treated Condition HBW
425 (≥) 314 (≥) 12 12 32 Solution and Aging, Annealing, Ausaging, Q+T,etc 321

Physical properties of grade Alloy L605

Property Density
kg/dm3		 Temperature T
°C/F		 Specific heat
J / kgK		 Thermal conductivity
W/mK		 Electric resistance
µΩ·cm
558 (≥) 979 (≥) 32 14 12 Solution and Aging, Annealing, Ausaging, Q+T,etc
Temp.
°C/°F		 Creep strain limit
(10000h)
(Rp1,0) N/mm2		 Creep rupture strength
(10000h)
(Rp1,0) N/mm2		 - - -
463 362 375 - - -

Alloy L605 Range of products
Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED