Grades | Special Alloy | K438
GBT K438
K438 Application:Age hardening type Nickel base alloy
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Mo(％) | W(%) | Co(%) | B(%) | Nb(%) | Al(%) | Ti(%) | Ta(%) | Other(%) |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 0.10-0.20 | Max 0.5 | Max 0.5 | Max 0.015 | Max 0.01 | 15.5-16.5 | Balance | 1.50-2.00 | 2.40-2.80 | 8.00-9.00 | 0.005-0.015 | 0.50-1.10 | 3.20-3.70 | 3.00-3.50 | 1.50-2.00 | Zr:0.05-0.15 |
| Yield Rp0.2 (MPa) |
Tensile Rm (MPa) |
Impact KV (J) |
Elongation A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | HBW |
|---|---|---|---|---|---|---|
| 547 (≥) | 374 (≥) | 33 | 42 | 24 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 144 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
|---|---|---|---|---|---|
| 278 (≥) | 643 (≥) | 43 | 13 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
- | - | - |
| 939 | 498 | 641 | - | - | - |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |