Grades | Superalloys | SB-637 N07750 Type 1
ASME SB-637 N07750 Type 1
PDF | Word | Print
SB-637 N07750 Type 1 Application:Precipitation-Hardening Nickel Alloy Bars, Forgings, and Forging Stock for High-Temperature Service
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.08 | ||
| Mn | - | 1.0 | ||
| Si | - | 0.5 | ||
| S | - | 0.01 | ||
| P | - | 0.015 | ||
| Cu | - | 0.5 | ||
| Fe | 5.0 | 9.0 | ||
| Co | - | 1.0 | ||
| Nb | 0.70 | 1.20 | ||
| Cr | 14.0 | 17.0 | ||
| Ni | 70 | - | ||
| Al | 0.40 | 1.00 | ||
| Ti | 2.25 | 2.75 |
| Yield Rp0.2 (MPa) |
Tensile Rm (MPa) |
Impact KV (J) |
Elongation A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | HBW |
|---|---|---|---|---|---|---|
| 129 (≥) | 855 (≥) | 34 | 11 | 41 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 314 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
|---|---|---|---|---|---|
| 475 (≥) | 182 (≥) | 11 | 43 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
- | - | - |
| 853 | 233 | 748 | - | - | - |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |