Grades | Special Alloy | XH51BMTЮKΦP(ЭП220)
ГОСТ XH51BMTЮKΦP(ЭП220)
XH51BMTЮKΦP(ЭП220) Application:Russia COST standard deformation of high temperature alloy
Chemical composition(mass fraction)(wt.%) of the XH51BMTЮKΦP(ЭП220)
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Mo(％) | V(%) | W(%) | Co(%) | B(%) | Al(%) | Ti(%) |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Max 0.08 | Max 0.50 | Max 0.50 | Max 0.015 | Max 0.009 | 9.0-12.0 | Balance | 5.0-8.0 | 0.2-0.8 | 5.0-7.0 | 14.0-16.0 | Max 0.02 | 3.9-4.8 | 2.2-2.9 |
Mechanical properties of grade XH51BMTЮKΦP(ЭП220)
| Yield Rp0.2 (MPa) |
Tensile Rm (MPa) |
Impact KV (J) |
Elongation A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | HBW |
|---|---|---|---|---|---|---|
| 232 (≥) | 529 (≥) | 44 | 13 | 12 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 333 |
Physical properties of grade XH51BMTЮKΦP(ЭП220)
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
|---|---|---|---|---|---|
| 812 (≥) | 774 (≥) | 23 | 24 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
- | - | - |
| 514 | 891 | 554 | - | - | - |
XH51BMTЮKΦP(ЭП220) Range of products
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |